Incoloy 926 strip has a similar chemical composition to austenitic stainless steel, but its nitrogen content is increased to about 0.2% and its molybdenum content is about 6.5%. The increase in nitrogen and molybdenum content significantly improves the resistance to pitting corrosion and crevice corrosion in halide media. Alloys with lower nitrogen content than nickel reduce the tendency of intergranular phase precipitation during hot processing or welding, especially in halogenated alloys. It has outstanding local corrosion resistance and excellent mechanical properties in physical media.
Specifications | In stock, can be customized according to customer requirements |
Form | Plate, rod, pipe, strip |
Classification | Nickel alloy |
|
Yield Strength(R0.2/ MPa) |
Tensile strength(R m /MPa） |
Elongationδ5 /% |
|
295 |
650 |
35 |
|
Physical Constants |
Density.g/cm² |
8.1 g/cm³ |
|
Melting Range |
1320-1390 ℃ |
|
Cr |
Ni |
Mo |
Fe |
C |
Si |
Mn |
P |
N |
|
20-21 |
24-26 |
6.0-7.0 |
Balance |
≤0.02 |
≤0.5 |
≤2.0 |
≤0.03 |
0.15-0.25 |
Incoloy 926 bar also has good corrosion resistance in other chemical media, as well as high temperature and high concentration media, including sulfuric acid, phosphoric acid, acid gas, seawater, salt, and organic acids.
926 alloy bar is a versatile material that can be used in many industrial fields:
1. Polished rods in corrosive oil wells
2. Hose system in marine engineering
3. Pipelines, joints, gas flow systems, etc. in acid gas production
4. Components in flue gas desulfurization system
5. Evaporators, heat exchangers, filters, mixers, etc. in phosphoric acid production
6. Sulfuric acid separation and condensation system
7. Evaporator for concentrating and crystallizing salt
8. Condensation and piping systems in power plants using sewage cooling water
The manufacturing process of stainless steel and alloys involves multiple steps to transform raw materials into flat,rectangular sheets or plates made of stainless steel and alloys. Here are a few key steps for stainless steel and alloys:
Molten stainless steel and alloys are cast into large ingots or billets through a casting process.
During the hot rolling process,the thickness of the steel ingot is gradually reduced and elongated to form long strips or coils.
Annealing involves heating stainless steel and alloys to a specific temperature and then slowly cooling it.
Cold rolling is carried out through rolling mills to reduce thickness to meet customer specifications.
Wuxi Walmay Metal Co,Ltd is a comprehensive processing group of Alloy Steel、Forged Parts Fitting、Titanium Alloy、Stainless Steel、Special Welding Wireseries， and more than 800 specifications.
Our group has been engaged in the domestic and global market for more than ten years with rich steel experience and can offer professional advice for customers inapplications with different materials.
Machine cutting
Sheet cutting
plasma cutting
Dynamic waterjet cutting
sawing
Plank leveling
polishing
laser cutting
laser cutting
production cutting
Long product cutting
Bar and structural cutting
polishing
Heat treatment and annealing: Wuxi Walmay Metal can heat treat certain 400 series stainless steels.
Material Reliability Identification (PMI): Wuxi Walmay Metal can complete this testing in-house.
Ut Testing: Ultrasonic testing (UT) uses high-frequency sound energy to inspect and measure stainless steel products.